KTH ALUMINIUM HEAT RESISTANCE PAINT 200°C, 300°C and 600°C is a aluminium primer based coating which can withstand continuous temperature 200°C, 300°C and 600°C. It is recommended for use in industrial chimney, heat exchanger and high temperature pipeline etc.
DUE TO MONITOR DIFFERENCES, ACTUAL COLOR MAY VARY SLIGHTLY FROM WHAT APPEARS ONLINE.
CONTACT US FOR COLOR SAMPLES IF YOU NEED HELP SELECTING A FINISH.
KTH 200°C HEAT RESISTANT ALUMINIUM PAINT
KTH 200°C HEAT RESISTANT ALUMINIUM PAINT is single component solvent based heat resistance aluminium paint. It is formulated with modified silicone resin and has atmospheric dry heat resistant up to 150°C, with occasional peak temperature up to 200°C. It gives silvery and low gloss finishing to painted surfaces.
Applications
- As primer, mid coat or top coat in a multi-coat coating system. Most suitable for use on properly prepared steel surfaces.
Composition
- Pigment: Aluminium paste.
- Binder: Silicone resin
- Solvent: Hydrocarbon
Physical Characteristics of the Paint
- Density : 0.96 – 1.02
- Volume Solid : 35 ± 5%
- Viscosity : 45 ± 5 KU at 30°C
- Theoretical Coverage : 10 – 13 m2 /litre
- Colour : Aluminium
Coating Properties
- Recommended Dry Film Thickness : 25 - 35 microns per coat
- Recommended Wet Film Thickness : 70 - 100 microns per coat
- Recommended Coating System : HR 200°C / HR 200°C
- Recommended Numbers of coat : One to two Drying Time : Touch Dry – 15 mins, Dry to handle – 1 hour
- Recoating interval : At least 8 hours
- Curing Time : 1 day
KTH 300°C HEAT RESISTANT ALUMINIUM PAINT
KTH 300°C HEAT RESISTANT ALUMINIUM PAINT is single component solvent based heat resistance aluminum paint. It is formulated with silicone resin and able to withstand continuous atmospheric dry heat resistant up to 250°C, and occasional peak temperature of 300°C. It gives silvery and low gloss finishing to painted surfaces.
Applications
- As primer, mid coat or top coat in a multi-coat coating system. Most suitable for use on properly prepared steel surfaces subject to extreme temperature.
Composition
- Pigment: Aluminium paste.
- Binder: Silicone resin
- Solvent: Hydrocarbon
Physical Characteristics of the Paint
- Density: 0.96 – 1.02
- Volume Solid: 43 ± 5%
- Viscosity: 49 ± 5 KU at 30°C
- Theoretical Coverage: 12.5 – 17 m2/litre
- Colour: Aluminium
Coating Properties
- Recommended Dry Film Thickness: 25 - 35 microns per coat
- Recommended Wet Film Thickness: 58 - 81 microns per coat
- Typical Coating System: HR 300°C / HR 300°C
- Recommended Numbers of coat: One to two
- Drying Time: Touch Dry – 15 mins, Dry to handle – 1 hour
- Recoating interval: At least 8 hours
- Curing Time: 1 day
KTH 600°C HEAT RESISTANT ALUMINIUM PAINT
KTH 600°C HEAT RESISTANT ALUMINIUM PAINT is single component solvent based heat resistance aluminium paint. It is formulated with silicone resin and able to withstand continuous atmospheric dry heat resistant up to 600°C. It gives silvery and low gloss finishing to painted surfaces.
Applications
- As primer, mid coat or top coat in a multi-coat coating system. Most suitable for use on properly prepared steel surfaces subject to extreme temperature.
Composition
- Pigment: Aluminium paste.
- Binder: Silicone resin
- Solvent: Hydrocarbon
Physical Characteristics of the Paint
- Density : 0.99 – 1.04
- Volume Solid : 37 ± 5%
- Viscosity : 49 ± 5 KU at 30°C
- Theoretical Coverage : 11 – 15 m2/litre
- Colour : Aluminium
Coating Properties
- Recommended Dry Film Thickness: 25 - 35 microns per coat
- Recommended Wet Film Thickness: 65 - 95 microns per coat
- Typical Coating System: HR 600°C / HR 600°C
- Recommended Numbers of coat: One to two
- Drying Time: Touch Dry – 15 mins, Dry to handle – 1 hour
- Recoating interval: At least 8 hours
- Curing Time: 1 day